202Cu stainless wire

Name: 202Cu stainless wire
Brand: Som Shanti Steels

Get a Price/Quote

MOQ : 50 Kilograms

202Cu stainless wire Specification

Corrosion Resistant
Yes

Heat Resistance
Yes

Recyclable
Yes

Material Composition %
Cr: 17-19%, Ni: 4-6%, Cu: 1.5-4%, Mn: 7.5-10%, C: 0.15%, Si: 1%, P: 0.06%, S: 0.03%

Hardness
HV 160 290 (depends on temper)

Tensile Strength
Typically 550-850 MPa

Product Form
Coil, spool, or straight length

Diameter
0.15 mm - 7.0 mm

Coating Type
Uncoated or as requested

Size
Customized

Product Name
202Cu Stainless Steel Wire

Steel Type
Stainless Steel

Steel Product Type
Wire

Grade
202Cu

Thickness
0.15 mm - 7.0 mm

Shape
Round

Steel Standard
ASTM, AISI, DIN, EN, GB, JIS

Surface
Bright, matt, or pickled finish

Composition
Nickel (Ni), Chromium (Cr), Manganese (Mn), Copper (Cu), Iron (Fe), Carbon (C), Silicon (Si), Phosphorus (P), Sulphur (S)

Application
Industrial, construction, wire mesh, weaving, and general-purpose use

Dimension (L*W*H)
Customized as per order

Weight
Varies as per coil and size

Color
Silver / Metallic

Material Grade
202Cu

Finish Type
Bright, Matt, Pickled

Usage
Weaving, welding rods, fasteners, general engineering

Density
~7.8 g/cm

Export Market
Worldwide

Magnetism
Non-magnetic in annealed condition, slightly magnetic after cold working

Available Tempers
Soft (annealed), 1/4 hard, 1/2 hard, full hard

Elongation
Minimum 35% (annealed)

Melting Range
1400 1450C

Packaging
Plastic spool, coils, or as per customer requirement

International Code
UNS S20200

202Cu stainless wire Trade Information

Minimum Order Quantity
50 Kilograms

Supply Ability
1000 Kilograms Per Week

Delivery Time
7 Days

About 202Cu stainless wire

SS 202Cu Wire High Strength Superior Quality At Som Shanti Steels we are proud to supply premiumgrade SS 202Cu Wire designed for optimal performance and versatility across a wide range of industrial applications Our SS 202Cu Wire stands out for its exceptional strength corrosion resistance and formability making it the perfect choice for demanding projects Key Features High Corrosion Resistance Engineered for durability even in harsh environments to ensure longterm reliability Excellent Strength Toughness Ideal for applications that require a combination of strength and flexibility Ease of Fabrication Easily welded and formed providing adaptability for various fabrication processes CopperEnhanced Alloy Enriched with copper content to enhance mechanical properties and resistance to work hardening Applications Construction and architectural projects Automotive and transportation components Industrial manufacturing Chemical processing equipment Household and kitchenware products Quality Assurance We adhere to the highest standards in quality control ensuring every batch of SS 202Cu Wire meets stringent specifications and exceeds customer expectations Trust Som Shanti Steels for reliable and superiorgrade stainless steel solutions tailored to your needs

High-Performance Alloy for Demanding Applications

202Cu stainless wire combines toughness, flexibility, and chemical durability for critical uses in weaving, welding rods, fasteners, and engineering. Its superior elongation (minimum 35% annealed) ensures adaptability under stress, while its corrosion resistance and heat tolerance make it ideal for environments where reliability is paramount. Its bright, matt, or pickled surface finish gives users options for aesthetic and functional needs.

Tailored Specifications and Global Availability

Customers worldwide benefit from the 202Cu stainless wire's customizable lengths, packaging formats, and temper grades, including annealed, quarter, half, or full hard. Whether for large-scale exports or specialized domestic projects, this wire is available in coils, spools, or straight lengths. Exporters and manufacturers offer responsive service to accommodate unique project specifications.

FAQ's of 202Cu stainless wire:

Q: How is 202Cu stainless steel wire packaged for delivery?

A: 202Cu stainless steel wire is supplied on plastic spools, in coils, or packaged according to specific customer requirements to ensure safe handling and transport.

Q: What are the main benefits of using 202Cu stainless wire in construction and industrial applications?

A: The wire's high elongation, excellent corrosion and heat resistance, and customizable size make it suitable for demanding environments, contributing to reliability and long-term performance in construction, wire mesh, and engineering uses.

Q: When does 202Cu stainless wire become slightly magnetic?

A: The wire is non-magnetic in its annealed condition but becomes slightly magnetic after undergoing cold working processes such as drawing or forming.

Q: Where can I use 202Cu stainless steel wire?

A: This wire is ideal for weaving, welding rods, fasteners, wire mesh manufacturing, and general engineering projects due to its adaptability and strength.

Q: How is the hardness of 202Cu wire adjusted?

A: The hardness varies based on temper grade-soft (annealed), 1/4 hard, 1/2 hard, and full hard-with typical Vickers hardness values ranging from 160 to 290, allowing users to select the right grade for their application.

Q: What is the standard composition of 202Cu stainless steel wire?

A: The wire is composed of Chromium (17-19%), Nickel (4-6%), Copper (1.5-4%), Manganese (7.5-10%), Carbon, Silicon, Phosphorus, and Sulphur within specified limits, meeting international material standards.